Oxygen vacancies induced band gap narrowing for efficient visible

Scientific Reports volume 13, Article number: 14105 (2023) Cite this article

Metrics details

The band gap of rutile TiO2 has been narrowed, via the formation of oxygen vacancies (OVs) during heat treatment in carbon powder (cHT) with embedding TiO2 coatings. The narrowed band gap efficiently improves the visible light response of TiO2 coatings, to further enhance the visible-light-driven photocatalytic activity. The change in OVs during cHT has been studied by manipulation of cHT temperature and time. The effect of OVs on the band structure of nonstoichiometric TiO2-x has been further calculated by first-principles calculations. With raising the temperature, SEM images show that the nano-size fiber-like structure forms on the surface of TiO2 coatings, and the amount of the fiber-like structure significantly increases and their size changes from nano to micro under 800 °C, contributing to cause an increase in accessible surface area. The UV–Vis results reveal that the band gap of TiO2 has been narrowed during cHT, due to the formed oxygen vacancies. The XPS results further confirm that the formation of surface defects including OVs, and the XPS depth profile further shows the decreased relative amount of O whereas increased relative amount of carbon. Notably, after cHT for TiO2 coatings, the photocatalytic activity first increases then decreases with raising the temperature, achieving approximately 3 times at 850 °C. The first-principles calculation suggest that the OVs in TiO2 coatings with localized electrons could facilitate the band gap narrowing, further favoring to enhance the photocatalytic activity under visible light.

Face to these urgent issues of environmental pollution and energy crisis, the use of renewable resources to develop renewable energy technologies is becoming an urgent subject that needs breakthroughs. Photocatalysis is considered as a candidate with great potential to alleviate and further solve these problems, because it can efficiently decompose organic pollutants or generate chemical energy via photocatalytic effect. Titanium dioxide (TiO2) can be regarded as one of the most important photocatalysts materials, because of the suitable band edge positions, outstanding stability, inexpensive and excellent photocatalytic activity1,2,3. However, TiO2 has been limited by its relative wide band gap (~ 3.2 eV of anatase or ~ 3.0 eV of rutile), for the visible light response4,5,6. Currently, tremendous efforts have been dedicated to improving the visible light absorption of TiO2, such as narrowing band gap with introduction of dopant or defects (OVs, Ti3+, lattice strains), and compositing with photocatalysts having smaller band gap or better visible light response7,8,9,10,11,12, to further meet the needs of practical applications. In addition, many pieces of literatures have reported that doping non-metals such as nitrogen, sulfur, or carbon into TiO2 lattice can extend the absorption edge from UV region to visible region, owing to the introduction of localized electronic states in the band gap13,14,15,16.

Notably, controllable doping of C impurities into TiO2 lattice is an effective approach to improve the photocatalytic activity, because that C can permeate into TiO2 lattice to substitute O or Ti atoms, accompanied by the formation of Ti–C or C–O–Ti bonds to generate hybrid orbitals above the valence band of TiO2, significantly inhibiting the recombination due to the transport channel and electron storage capacity. After Khan et al. reported the carbon substitutes for the lattice oxygen atoms in TiO2 with a lower band gap about 2.32 eV in 200217, many researchers have successively proven that C doped TiO2 is an effective strategy to narrow the band gap and generate surface defects such as OVs, to further enhance the visible-light-driven photocatalytic activity18,19,20,21,22.

Apart from doping, OVs-induced photocatalysis is another efficient solution to achieve visible-light response, charge separation simultaneously, to serve as active site for the adsorption and subsequent dissociation of O-containing molecules. In 2000, Nakamura et al. investigated the role of OVs in TiO2 photocatalyst that locate between the valence and the conduction bands, for visible light response23, then Schaub et al. unraveled the diffusion mechanism of OVs on rutile TiO2 in 200224. Wendt et al. reported that OVs could significantly promote the charge separation, by the induced hole trapping25. From the perspective of electronic structure analysis, it is generally believed that OVs can improve the electronic structure of metal oxide semiconductors with introducing some kinds of defect states (such as Ti3+, point defect) below the conduction band and narrowing the band gap for better visible-light response26,27. More important, the amount of OVs plays a key role on the visible light response and improved photocatalytic activity of TiO2 from experimental measurements and theoretical calculations28,29,30,31.

In this work, to investigation of the formed OVs during cHT and further enhance the photocatalytic activity of TiO2, we focus on adjusting the OVs in C-doped TiO2 by manipulation of cHT temperature and time. It reveals that the formation of OVs in the surface is significant with raising cHT temperature, compared with that of extending cHT time. In addition, the influence of cHT on the crystal structure, surface morphology, and their photocatalytic activity is analyzed and revealed.

The fabrication of photocatalyst coatings was carried out by coating formation, oxidation and cHT process. Firstly, Ti coatings were formed on Al2O3 balls (93.0% for purity, 1 mm for average diameter, Nikkato) by machinal coating technique, using Ti powder (99.1% for purity, 30 μm for average diameter, Osaka Titanium technologies), donated as "Ti". The details of MCT operation refer to the previous studies32,33,34,35. Then, the as-prepared Ti coatings were oxidized at 800 °C for 15 h in the atmosphere with a furnace (HPM-1G, As one), to generate rutile TiO2, donated as "TiO2". Followed the oxidation, the cHT for TiO2 coatings were conducted with embedding in carbon powder (150 μm for average diameter) using a short alumina pipe, and annealed with the same electric furnace, at x (650–1000 °C, with an interval of 50 C) for 0.1, 0.5 and 1 h, respectively. The samples were kept in the furnace until approximately 25 °C, and donated as "cHT-x℃yh", where x is the temperature and y is the time during the cHT.

The compounds and phase change of the prepared photocatalyst coatings were examined by an X-ray diffraction (XRD, JDX-3530) with Cu-Kα radiation, with the 2θ range from 23 to 65 deg (the step is 0.02 deg/s). The evolutions of surface morphology were observed using a scanning electron microscopy (SEM, Hitachi-SU8030). The chemical composition on the surface were investigated using X-ray photoelectron spectroscopy (XPS, PHI Quantes). UV–Vis absorption spectra were recorded using an ultraviolet–visible spectrophotometer (DRUV-vis, Shimadzu 3700/3700DUV). The evaluation of photocatalytic activity was carried out with the photodecomposition of methylene blue (MB) solution under visible light and UV irradiation at approximately 25 °C. According to the ISO 10678-2010, all samples were firstly dried under UV light for 24 h, then the potential absorption was avoided by soaking within MB solution (20 μmol/L, 35 mL) for 18 h in dark. The samples were evenly laid on the bottom of the cell for the photodecomposition test, and the initial concentration of MB solution was 10 μmol/L. The irradiation intensity of visible light (λ greater than 420 nm) and UV on the samples were set as 5000 lx and 1.0 mW/cm2, respectively. The absorbance of MB solution was measured by a colorimeter (mini Photo 10, Sanshin), with the absorption peak around 660 nm. The details of the photocatalytic evaluation can be found in our published works33,34,35. The difference in degradation constant (R) between ksample and kMB-solution was further used to highlight the photocatalytic activity of the samples.

To further investigate the relationship between surface OVs in TiO2 lattice and band gap, the electronic structure calculations were performed to calculate rutile TiO2-x surfaces with different contents of OVs by the PHASE based on the framework of density functional theory (DFT)36,37, within a program code using plane-wave basis sets based on the pseudopotential method. The difficulty is to alter the stoichiometry of TiO2-x that determines the electronic band structures38. Consequently, the electronic structure calculations of rutile TiO2 and nonstoichiometric TiO2-x (TiO1.958, TiO1.917, TiO1.875, and TiO1.600) were carried out and investigated. The details of condition calculations refer to the previous studies37. The structure parameters of both TiO2-x are shown in Supplementary Table S1. A plane-wave cutoff with 340 eV was applied during these calculations, while the convergence in self-consistent field was 27 × 10–7 eV. Supplementary Table S2 presents the related main parameters for the calculations.

XRD patterns of the as-prepared samples are presented in Fig. 1, together with the Raman results of the cHT-x℃0.5 h samples. From the Ti sample, it could find that Ti coatings (approximately 50–70 μm39,40) were coated on each Al2O3 ball. While the diffraction peaks at 27.4°, 36.1°, 41.2°, and 54.3° from the TiO2 samples show that rutile TiO2 successfully form on the surface of Ti coatings after oxidization at 800 °C for 15 h. Figure 1a, with raising the cHT temperature for relative short time of 0.1 h. However, it hard to observe the change even at high temperature of 1000 °C. While extending the cHT time to 0.5 h, the rutile TiO2 keeps until the temperature up to 850 °C, then it starts to change, especially at peak of 27.4°, which indicates that the new compounds exhibited Magneli phases that appear to have formed29,37,41,42,43,44. To further investigate the cHT time at different temperature, the change in crystal structure of the cHT-x℃1 h samples is similar to those of the cHT-x℃0.5 h samples. The Magneli phases of Ti4O7 and Ti3O5 become to replace rutile at 1000 °C for 1 h, as shown in Fig. 1. It could conclude that the influence on rutile TiO2 becomes to be found from cHT temperature of 900 °C, simultaneously the cHT time also needs to have a minimum limit. In addition, the grain sizes of the cHT-x℃0.5 h samples increase before the formation of Magneli phases (Supplementary Table S3). Similar to that of the XRD result, it is hardly to find the change in Raman spectra from the cHT-x℃0.1 h samples (Supplementary Fig. S1), owing to the too short cHT time. It starts to change at 900 °C for at least 0.5 h. Back to the cHT-x℃0.5 h samples, Fig. 1d shows that the rutile TiO2 significantly starts to change at 900 °C then to be Magneli phases at 1000 °C45,46, which is also well matched with those of XRD results.

XRD patterns and Raman spectra of the samples. (a) cHT-x℃0.1 h, (b) cHT-x℃0.5 h, (c) cHT-x℃1 h, and (d) cHT-x℃0.5 h.

Figure 2 presents the surface morphology evolution of the cHT-x℃0.5 h samples. It could be observed that a typical columnar structure of rutile TiO2 has been formed, as shown in Fig. 2a 29,32,33,34,35,41,46,47. Compared to that of TiO2, it is clearly found that the change in surface morphology of the cHT-x℃0.5 h samples, with raising the cHT temperature. Interesting, a large amount of nano-size needle-like structures are formed during the cHT, with a temperature below 900 °C. From Fig. 2b,c, the needle-like structures are mixed with the columnar structure. With further raising the temperature, the nano-size needle-like structures grow in number and size. Compared with Fig. 2a–g, it reveals that the nano-size needle-like structures are generated with breaking of the columnar structure. While the temperature is higher than 900 °C, due to the generated Magneli phases, a completely different morphology has been formed, replacing those of the needle-like and columnar structures. With the change in the surface morphology caused by the formed compounds and their crystal structures during cHT, it inevitably has a direct impact on its accessible area, which in turn has an impact on the photocatalytic performance.

Surface morphology comparison of the TiO2 and cHT-x℃0.5 h samples. (a) TiO2, (b) cHT-650℃0.5 h, (c) cHT-700℃0.5 h, (d) cHT-750℃0.5 h, (e) cHT-800℃0.5 h, (f) cHT-850℃0.5 h, (g) cHT-900℃0.5 h, (h) cHT-950℃0.5 h, and (i) cHT-1000℃0.5 h.

UV–Vis spectroscopy is used to study the electronic states of the cHT-x℃0.5 h samples. Figure 3a shows a typical and strong absorbance behavior in UV region and very weak absorption in visible light region, from the TiO2 sample. With raising the cHT temperature to 650 and 700 °C, the absorbance edge around 400–420 nm evidently moves towards the visible light range. While further raising the temperature up to 800 °C, the absorbance behavior of the samples strongly increases, especially within the visible region, which could be related to the increased amount of the formed OVs23,24,25,28,29,30,31, during cHT with raising the temperature. Notably, in the case of 850 °C, it prominently indicates the significantly moved absorbance edge and strongly increased visible-light response. This proves that cHT is a pivotal role in the absorbance redshift. Moreover, the appearance is more directly show the effect of cHT on the light absorbance (Supplementary Fig. S2). When the temperature is higher than 850 °C, it could find that the absorbance completely changes, attributing to the formed Magneli phases of Ti4O7 and/or Ti3O5, having a graphite-like conductivity at room temperature29,37,42,43. It means that the band gap of the samples with Magneli phases might be nearly zero eV, which is well matched with the observed absorption from Fig. 3a.

UV–Vis absorption spectra (a) and plot of (αhv)2 against hv of the cHT-x℃0.5 h samples.

To clearly show the influence of cHT on the band gap, the corresponding Kubelka–Munk plots are shown as Fig. 3b. The change in band gap is slow when the temperature is lower than 800 °C, and the calculated band gap is summarized in Supplementary Table S3. When the temperature is up to 850 °C, the band gap is significantly narrowed to 2.879 eV, from 2.984 of the TiO2 sample, due to the generated OVs in lattice of rutile TiO2 during cHT.

XPS spectra was further carried out to study the surface chemical bonding of the cHT-x℃0.5 h samples, as illustrated in Fig. 4. In general, the change in C 1 s and Ti 2p is hard to be found, while it is significant in the case of O 1 s, especially in OVs from the cHT-700℃0.5 h and cHT-800℃0.5 h samples. Basically, the peak at approximately 529.8 eV presented with black line in Fig. 4b could be attributed to the O2− ions, usually surrounded by Ti4+ ions in rutile TiO234,47,48,49,50. The asymmetric peaks of O 1 s could be attributable to the three contributions different chemical states, such as the above O2− ions, OVs (around 531.0 eV)23,24,25,28,29,30,31 and loosely bound oxygens at grain boundaries or the chemisorbed oxygens (around 532.2 eV)51,52,53. It could be found that a slight change in the O 1 s peak from 529.8 eV of rutile TiO2 to 530.0 eV of the cHT-1000℃0.5 h sample, which hints that the possible formation of Ti3+ neighboring to OVs in rutile TiO224,25,26,29. The shift in Ti 2p peak also suggests the formation of Ti3+20. What’s more, the peak change around 531.0 eV incidents that the amount of OVs increase, with raising the cHT temperature. According to the XRD and XPS results, it could conclude that the rutile TiO2 on the outer surface starts to react with the involved carbon and its compounds during cHT at 700 °C, while the increased amount of OVs formed and discussed into the bulk of TiO2 films at higher temperature, which will affect the crystal structure (Fig. 1).

XPS spectra of the cHT-x℃0.5 h samples.

Furthermore, to better understand the effect of cHT for TiO2 films on the change in surface elements, XPS depth profile measurements were performed on the cHT-x℃0.5 h samples, giving the atomic percentage of namely C, Ti, and O, as shown in Fig. 5. The results indicant that the changes in C and O are significant in the outer surface, whereas Ti is relatively stable. Notably, it shows that the relative amount of C increases and O decreases in the outer surface with raising cHT temperature, revealing the C has successfully doped into the surface of TiO2 films and resulted in the formation of OVs easily occurs at higher 800 °C15,16,17,18,19,20,21,34. While the amount of O from the cHT-1000℃0.5 h sample drops below 40% and is significantly lower compared to other samples, which could be attributed to the formation of the Magneli phase.

XPS depth profile of the cHT-x℃0.5 h samples.

For the photodegradation of MB solution presented with the samples, Fig. 6 clearly reveals that the cHT could efficiently enhance the visible-light-driven photocatalytic activity (Supplementary Fig. S3), and same in the case of UV irradiation (Supplementary Fig. S4). The hardly decreased blank dotted line hints that the MB solution is relatively stable. In general, with raising the cHT temperature or extending the cHT time, it demonstrates that the photocatalytic activity firstly increases then decreases due to the concentration change of MB solution. Compared with that of extending the cHT time, it seems that raising the cHT temperature is more efficiently improve the photocatalytic activity with 0.1 h. Figure 6d more directly shows that the changes in degradation constant (R), with all cHT condition. In the case of 0.1 h, the photocatalytic activity keeps enhancing until the cHT temperature reached 850 °C, whereas for the longer cHT time of 0.5 h and 1 h, the photocatalytic activity starts to decrease when the temperature is higher than 800 °C. In other words, the photocatalytic activity could be enhanced at a relative higher temperature for shorter time. It is well known that the doping of metal or nonmetal ions is often accompanied by formation of OVs in the lattice of TiO218,19,20,21. Numerous studies have reported that the presence of OVs in TiO2 can located at 0.75–1.18 eV below the conduction band minimum, to effectively expand the visible light absorption range7,8,9,23,24,25. The enhanced visible-light-driven photocatalytic activity could be attributed to the visible-light response due to the narrowed band gap (especially under 850 °C in Fig. 3), and the increased accessible area due to the formed nano-size needle-like structures on the surface until disappearing around 850 °C (Fig. 2). Correspondingly, when the temperature is higher than 850 °C, the decreases in the photocatalytic activity at are mainly because of the formed Magneli phases (Fig. 1)29,54,55, and the destroyed needle-like structures on the surface.

Concentration evolution of MB solution under visible light for the cHT-x℃yh samples. (a) 0.1 h, (b) 0.5 h, (c) 1 h and (d) Degradation constant R between ksample and kMB-solution.

While comparing the cHT time under different temperature, the time is necessary at lower temperature of 650 °C, then the temperature will dominant the enhancement of visible-light-driven photocatalytic activity, compared with that of time. Notably, the advantage of cHT temperature for 0.1 h is more prominent above 800 °C, and the R of cHT-850℃0.1 h is further improves by about 3 times, compared with that of TiO2. Moreover, the photocatalytic activity under UV irradiation could be further enhanced at 800 to 850 °C for 0.5 h.

To further investigate the effect of OVs on the visible-light response of TiO2, the DFT method was adopted to calculate the stoichiometric and non-stoichiometric rutile TiO2 (110) surfaces. The effect of OVs on the total density of states (TDOS) of TiO2-x (x: 0, 0.042, 0.083, 0.125 and 0.400) are presented in Fig. 7. In general, a high vacancy concentration could induce a vacancy band of electronic states just below the conduction band, which had been confirmed by theoretical calculations and relevant experiments37,56,57,58. Interestingly, Fermi level significantly shifts toward the conduction band with the increased amount of OVs, which indicates that the introduction of OVs results in two loosely captured electrons by three Ti dangling bonds23,27,29,37,56. Moreover, the band gaps of TiO2-x start to decrease from TiO1.917, by about 0.02–0.5 eV with respect to 1.88 eV from pure TiO2, which is consistent with previous study37,57,58.

TDOS of TiO2 and TiO2-x near Fermi level. The Fermi level during the calculation was set as zero. The red dotted line represents valence band maximum (VBM), while the blue dotted line is conduction band maximum (CBM).

In this study, the OVs induced visible-light response C-doped TiO2 photocatalyst films with were successfully prepared by a simple and efficient method of cHT for TiO2 formed on Ti coatings. The visible-light-driven photocatalytic activity of C-doped TiO2 has been significantly enhanced by around 3 times, compared with that of pure TiO2. With raising the cHT temperature under 850 °C, the surface morphology with nano-size needle-like structures forms that could significantly increase the accessible surface area, while the needle-like structures would disappear at higher temperature. Generally, with raising the cHT temperature or extending the cHT time, it demonstrates that the photocatalytic activity firstly increases then decreases, reaching a better photocatalytic activity under 850 °C for 0.1 h. The enhanced visible-light-driven photocatalytic activity could be attributed to the improved visible-light response due to the narrowed band gap, and the increased accessible area due to the formed nano-size needle-like structures. Compared with cHT time, the photocatalytic activity could be enhanced at a relative higher temperature for shorter time. Notably, the introduction of OVs results in substantially narrowing band gap of TiO2-x, compared with that of pure TiO2.

All data generated or analysed during this study are included in this published article (and its supplementary information files).

Henderson, M. A. A surface science perspective on TiO2 photocatalysis. Surf. Sci. Rep. 66, 185–297 (2011).

Article ADS CAS Google Scholar

Guo, Q., Zhou, C., Ma, Z. & Yang, X. Fundamentals of TiO2 photocatalysis: Concepts, mechanisms, and challenges. Adv. Mater. 31, 1901997 (2019).

Article CAS Google Scholar

Li, Z., Wang, S., Wu, J. & Zhou, W. Recent progress in defective TiO2 photocatalysts for energy and environmental applications. Renew. Sustain. Energy Rev. 156, 111980 (2019).

Article Google Scholar

Etacheri, V., Valentin, C. D., Schneider, J., Bahnemann, D. & Pillai, S. C. Visible-light activation of TiO2 photocatalysts: Advances in theory and experiments. J. Photochem. Photobiol. C 25, 1–29 (2015).

Article CAS Google Scholar

Kusiak-Nejman, E. & Morawski, A. W. TiO2/graphene-based nanocomposites for water treatment: A brief overview of charge carrier transfer, antimicrobial and photocatalytic performance. Appl. Catal. B 253, 179–186 (2019).

Article CAS Google Scholar

Wu, S., Li, X., Tian, Y., Lin, Y. & Hu, Y. Excellent photocatalytic degradation of tetracycline over black anatase-TiO2 under visible light. Chem. Eng. J. 406, 126747 (2021).

Article CAS Google Scholar

Li, D., Haneda, H., Labhsetwar, N. K., Hishita, S. & Ohashi, N. Visible-light-driven photocatalysis on fluorine-doped TiO2 powders by the creation of surface oxygen vacancies. Chem. Phys. Lett. 401, 579–584 (2005).

Article ADS CAS Google Scholar

Wu, Q. & Krol, R. V. D. Selective photoreduction of nitric oxide to nitrogen by nanostructured TiO2 photocatalysts: Role of oxygen vacancies and iron dopant. J. Am. Chem. Soc. 134, 9369–9375 (2012).

Article CAS PubMed Google Scholar

Setvin, M. et al. Reaction of O2 with subsurface oxygen vacancies on TiO2 anatase (101). Science 341, 988–991 (2013).

Article ADS CAS PubMed Google Scholar

Xiu, Z. et al. Recent advances in Ti3+ self-doped nanostructured TiO2 visible light photocatalysts for environmental and energy applications. Chem. Eng. J. 382, 123011 (2020).

Article CAS Google Scholar

Zhou, L., Zhang, X., Cai, M., Cui, N. & Chen, G. New insights into the efficient charge transfer of the modified-TiO2/Ag3PO4 composite for enhanced photocatalytic destruction of algal cells under visible light. Appl. Catal. B Environ. 302, 120868 (2022).

Article CAS Google Scholar

Yuan, J. et al. Template-free synthesis of core-shell Fe3O4@MoS2@mesoporous TiO2 magnetic photocatalyst for wastewater treatment. Int. J. Miner. Metall. Mater. 30, 177–191 (2023).

Article CAS Google Scholar

Wang, Y., Feng, C., Zhang, M., Yang, J. & Zhang, Z. Visible light active N-doped TiO2 prepared from different precursors: Origin of the visible light absorption and photoactivity. Appl. Catal. B 104, 268–274 (2011).

Article CAS Google Scholar

Gao, H., Liu, Y., Ding, C., Dai, D. & Liu, G. Synthesis, characterization, and theoretical study of N, S-codoped nano-TiO2 with photocatalytic activities. Int. J. Miner. Metall. Mater. 18, 606–614 (2011).

Article CAS Google Scholar

Varnagiris, S., Medvids, A., Lelis, M., Milcius, D. & Antuzevics, A. Black carbon-doped TiO2 films: Synthesis, characterization and photocatalysis. J. Photochem. Photobiol. A Chem. 382, 111941 (2019).

Article CAS Google Scholar

Han, Q. et al. Rational design of high-concentration Ti3+ in porous carbon-doped TiO2 nanosheets for efficient photocatalytic ammonia synthesis. Adv. Mater. 33, 2008180 (2021).

Article CAS Google Scholar

Khan, S. U. M., Al-Shahry, M. & Ingler, W. B. Jr. Efficient photochemical water splitting by a chemically modified n-TiO2. Science 297, 2243–2245 (2002).

Article ADS CAS PubMed Google Scholar

Irie, H., Watanabe, Y. & Hashimoto, K. Carbon-doped anatase TiO2 powders as a visible-light sensitive photocatalyst. Chem. Lett. 32, 772–773 (2003).

Article CAS Google Scholar

Ren, W. et al. Low temperature preparation and visible light photocatalytic activity of mesoporous carbon-doped crystalline TiO2. Appl. Catal. B 69, 138–144 (2007).

Article CAS Google Scholar

Shoji, S., Yamaguchi, A., Sakai, E. & Miyauchi, M. Strontium titanate based artificial leaf loaded with reduction and oxidation cocatalysts for selective CO2 reduction using water as an electron donor. ACS Appl. Mater. Interfaces. 9, 20613–20619 (2017).

Article CAS PubMed Google Scholar

Wang, G. et al. An antibacterial platform based on capacitive carbon-doped TiO2 nanotubes after direct or alternating current charging. Nat. Commun. 9, 2055 (2018).

Article ADS PubMed PubMed Central Google Scholar

Han, X. et al. Ti3C2 MXene-derived carbon-doped TiO2 coupled with g-C3N4 as the visible-light photocatalysts for photocatalytic H2 generation. Appl. Catal. B Environ. 265, 118539 (2020).

Article CAS Google Scholar

Nakamura, I. et al. Role of oxygen vacancy in the plasma-treated TiO2 photocatalyst with visible light activity for NO removal. J. Mol. Catal. A Chem. 161, 205–212 (2000).

Article CAS Google Scholar

Schaub, R. et al. Oxygen-mediated diffusion of oxygen vacancies on the TiO2 (110) surface. Science 299, 377–379 (2002).

Article ADS PubMed Google Scholar

Wendt, S. et al. The role of interstitial sites in the Ti3d defect state in the band gap of titania. Science 320, 1755–1759 (2008).

Article ADS CAS PubMed Google Scholar

Zuo, F. et al. Self-doped Ti3+ enhanced photocatalyst for hydrogen production under visible light. J. Am. Chem. Soc. 132, 11856–11857 (2010).

Article CAS PubMed Google Scholar

Anandan, S. & Miyauchi, M. Ce-doped ZnO (CexZn1−xO) becomes an efficient visible-light-sensitive photocatalyst by co-catalyst (Cu2+) grafting. Phys. Chem. Chem. Phys. 13, 14937–14945 (2011).

Article CAS PubMed Google Scholar

Anandan, S., Ohashi, N. & Miyauchi, M. ZnO-based visible-light photocatalyst: Band-gap engineering and multi-electron reduction by co-catalyst. Appl. Catal. B 100, 502–509 (2010).

Article CAS Google Scholar

Hao, L., Miyazawa, K., Yoshida, H. & Lu, Y. Visible-light-driven oxygen vacancies and Ti3+ co-doped TiO2 coatings prepared by mechanical coating and carbon reduction. Mater. Res. Bull. 97, 13–18 (2018).

Article CAS Google Scholar

Zhang, Y. et al. Direct observation of oxygen vacancy self-healing on TiO2 photocatalysts for solar water splitting. Angewandte Chemie Int. Ed. 58, 14229–14233 (2019).

Article CAS Google Scholar

Bi, X. et al. Tuning oxygen vacancy content in TiO2 nanoparticles to enhance the photocatalytic performance. Chem. Eng. Sci. 234, 116440 (2021).

Article CAS Google Scholar

Lu, Y., Guan, S., Hao, L. & Yoshida, H. Review on the photocatalyst coatings of TiO2: Fabrication by mechanical coating technique and its application. Coatings 5, 425–464 (2015).

Article CAS Google Scholar

Guan, S. et al. Enhanced photocatalytic activity of photocatalyst coatings by heat treatment in carbon atmosphere. Mater. Lett. 167, 43–46 (2016).

Article CAS Google Scholar

Guan, S. et al. Influence of heat treatment process on photocatalytic activity of photocatalyst TiO2/TiCxOy coatings during heat treatment in carbon powder. J. Mater. Sci. Mater. Electron. 27, 10399–10404 (2016).

Article CAS Google Scholar

Guan, S. et al. Fabrication of oxygen-deficient TiO2 coatings with nano-fiber morphology for visible-light photocatalysis. Mater. Sci. Semicond. Process. 41, 358–363 (2016).

Article CAS Google Scholar

Asari, Y., Nara, J. & Ohno, T. Theoretical study on diffusion mechanism of fluorine atom adsorbed on Si (111) reconstructed surface. Surf. Sci. 1–2, 225–231 (2011).

Article ADS Google Scholar

Wang, L. et al. Nonstoichiometric TiO2-x obtained via spark plasma sintering: Thermoelectric properties and first-principles calculations. J. Mater. Sci. 57, 15213–15223 (2022).

Article ADS CAS Google Scholar

Zebarjadi, M., Esfarjani, K., Dresselhaus, M. S., Ren, Z. & Chen, G. Perspectives on thermoelectrics: From fundamentals to device applications. Energy Environ. Sci. 5, 5147–5162 (2012).

Article Google Scholar

Guan, S. et al. Fabrication and characterization of photocatalyst composite coatings of TiO2/TiC-Ti using Ti and TiC powders. Surf. Coat. Technol. 307, 627–632 (2016).

Article CAS Google Scholar

Lu, Y. et al. Influence of oxidation process on photocatalytic activity of photocatalyst coatings by mechanical coating technique. Mater. Sci. Semicond. Process. 30, 128–134 (2015).

Article CAS Google Scholar

Toyoda, M. et al. Preparation of carbon-coated Magneli phases TinO2n-1 and their photocatalytic activity under visible light. Appl. Catal. B Enviorn. 88, 160–164 (2009).

Article CAS Google Scholar

Harada, S., Tanaka, K. & Inui, H. Thermoelectric properties and crystallographic shear structures in titanium oxides of the Magnèli phases. J. Appl. Phys. 108, 083707 (2010).

Article ADS Google Scholar

Takimoto, D., Toda, Y., Tominaka, S., Mochizuki, D. & Sugimoto, W. Conductive nanosized Magnéli-phase Ti4O7 with a core@shell structure. Inorg. Chem. 58, 7062–7068 (2019).

Article CAS PubMed Google Scholar

Shi, H. et al. Degradation of perfluorooctanesulfonate by reactive electrochemical membrane composed of Magnéli phase titanium suboxide. Environ. Sci. Technol. 53, 14528–14537 (2019).

Article ADS CAS PubMed Google Scholar

Yao, S. et al. Synthesis, characterization, and electrochemical performance of spherical nanostructure of Magneli phase Ti4O7. J. Mater. Sci. Mater. Electron. 28, 7264–7270 (2017).

Article CAS Google Scholar

Jiao, W. et al. Synthesis of mesoporous single crystal rutile TiO2 with improved photocatalytic and photoelectrochemical activities. Chem. Commun. 100, 11770–11772 (2013).

Article Google Scholar

Bourikas, K., Kordulis, C. & Lycourghiotis, A. Titanium dioxide (anatase and rutile): Surface chemistry, liquid-solid interface chemistry, and scientific synthesis of supported catalysts. Chem. Rev. 114, 9754–9823 (2014).

Article CAS PubMed Google Scholar

Guan, S. et al. Significantly enhanced photocatalytic activity of TiO2/TiC coatings under visible light. J. Solid State Electrochem. 22, 3183–3190 (2018).

Google Scholar

Colon, G. et al. Structural and surface approach to the enhanced photocatalytic activity of sulfated TiO2 photocatalyst. Appl. Catal. B 63, 45–59 (2006).

Article CAS Google Scholar

Sakamoto, K., Hayashi, F., Sato, K., Hirano, M. & Ohtsu, N. XPS spectral analysis for a multiple oxide comprising NiO, TiO2, and NiTiO3. Appl. Surf. Sci. 526, 146729 (2020).

Article CAS Google Scholar

Yang, S., Zhu, W., Jiang, Z., Chen, Z. & Wang, J. The surface properties and the activities in catalytic wet air oxidation over CeO2–TiO2 catalysts. Appl. Surf. Sci. 252, 8499–8505 (2006).

Article ADS CAS Google Scholar

Anandan, S. & Miyauchi, M. Improved photocatalytic efficiency of a WO3 system by an efficient visible-light induced hole transfer. Chem. Commun. 48, 4323–4325 (2012).

Article CAS Google Scholar

Zhang, C., Li, Y., Wang, Y. & He, H. Sodium-promoted Pd/TiO2 for catalytic oxidation of formaldehyde at ambient temperature. Environ. Sci. Technol. 48, 5816–5822 (2014).

Article ADS CAS PubMed Google Scholar

Domaschke, M. et al. Magnéli-phases in anatase strongly promote cocatalyst-free photocatalytic hydrogen evolution. ACS Catal. 9, 3627–3632 (2019).

Article CAS Google Scholar

Wierzbicka, E. et al. Magnéli phases doped with Pt for photocatalytic hydrogen evolution. ACS Appl. Energy Mater. 2, 8399–8404 (2019).

Article CAS Google Scholar

Hao, L., Huang, H., Zhang, Y. & Ma, T. Oxygen vacant semiconductor photocatalysts. Adv. Funct. Mater. 31, 2100919 (2021).

Article CAS Google Scholar

Yang, K., Dai, Y. & Huang, B. Understanding photocatalytic activity of S- and P-doped TiO2 under visible light from first-principles. J. Phys. Chem. 111, 18985–18994 (2007).

CAS Google Scholar

Zhang, J., Zhou, P., Liu, J. & Yu, J. New understanding of the difference of photocatalytic activity among anatase, rutile and brookite TiO2. Phys. Chem. Chem. Phys. 16, 20382–20386 (2014).

Article CAS PubMed Google Scholar

Download references

Research Center for Space System Innovation, Tokyo University of Science, Chiba, Japan

Sujun Guan & Chiaki Tarashima

Beijing Key Laboratory of Biomass Waste Resource Utilization, Beijing Union University, Beijing, China

Yanling Cheng

College of Mechanical Engineering, Tianjin University of Science and Technology, Tianjin, China

Liang Hao

Chiba Industrial Technology Research Institute, Chiba, Japan

Hiroyuki Yoshida

Bio-Nano Electronics Research Centre, Toyo University, Saitama, Japan

Tianzhuo Zhan

Graduate School and Faculty of Engineering, Chiba University, Chiba, Japan

Takaomi Itoi, Tangbin Qiu & Yun Lu

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

You can also search for this author in PubMed Google Scholar

S.G.: Research idea, experimental implementation, data analysis and discussion, and write and revise the manuscript. Y.C.: Data discussion and revise the manuscript.L.H.: Data discussion and editing draft.H.Y.: Data discussion.C.T.: Data discussion.T.Z.: Experimental implementation and data discussion.T.I.: Data discussion and editing draft. T.Q.: Experimental implementation.Y.L.: Data discussion, original draft preparation, supervision.

Correspondence to Yanling Cheng or Yun Lu.

The authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Reprints and Permissions

Guan, S., Cheng, Y., Hao, L. et al. Oxygen vacancies induced band gap narrowing for efficient visible-light response in carbon-doped TiO2. Sci Rep 13, 14105 (2023). https://doi.org/10.1038/s41598-023-39523-6

Download citation

Received: 09 May 2023

Accepted: 26 July 2023

Published: 29 August 2023

DOI: https://doi.org/10.1038/s41598-023-39523-6

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.